Contrast Enhancement Coatings
Anti-Glare Hard Coating Performance Specifications
| Scratch (Abrasion) Resistance |
| 75 and 54 Gloss High Resolution Diffusion-Hard Coats (HRD-HC) |
| |
Haze% (1) |
| |
Uncoated |
Coated |
| Steel-Wool Scratch (2) |
31.1 |
0.4 |
| Taber Abrasion (3) |
26.2 |
3-4 (4) |
|
| 1) |
Haze: ASTM D-1003 |
| 2) |
Steel-Wool Scratch: Steel-wool rotary test representing severe scratching using a #0000 steel-wool pad at 24 psi for 100 rotations. |
| 3) |
Taber Abrasion: ASTM D-1044 (CS10F wheel with 500-gram load). |
| 4) |
100 Cycles |
|
| 35 and 50 Gloss Ultra High Resolution Diffusion-Hard Coats (UHRD-HC) |
| |
Haze % (1) |
| |
Uncoated |
Coated |
| Steel-Wool Scratch (2) |
31.1 |
No Scratches |
| Taber Abrasion (3) |
26.2 |
.75 (4), 4 (5) |
|
| 1) |
Haze: ASTM D-1003 |
| 2) |
Steel-Wool Scratch: Steel-wool rotary test representing severe scratching using a #0000 steel-wool pad at 24 psi for 100 rotations. |
| 3) |
Taber Abrasion: ASTM D-1044 (CS10F wheel with 500-gram load). |
| 4) |
100 Cycles |
| 5) |
500 Cycles |
|
| Chemical Resistance |
| |
75 and 54 Gloss |
50 and 35 Gloss |
Gasoline
Toluene
Acetone
Ethanol
Trichloroethylene
5% Ammonia
10% Caustic Soda
50% Caustic Soda
10% Sulfuric Acid |
M
S
S
L
S
S
S
S
L |
M
M
M
L
S
M
M
S
L |
L-Long Term Contact,24+ hours
S-Short-term contact, up to 1 hour |
M-Medium-term contact, up to 8 hours
X-Immediate attack |
| Note: Testing done per ASTM D1308 |
|
| Coating Composition |
| 54 and 75 Gloss |
50 and 35 Gloss |
Organic Cross Linked Acrylic
Spray Coated
Radiation Cured (UV) |
Inorganic Siloxane
Flow Coated
Thermally Cured |
|
|
|